Having said that, this peak at ~978 nm was observed in both equally iron-doped and -undoped ZnSe solitary crystals, and its built-in intensity was higher while in the iron-undoped sample in contrast with the iron-doped sample. As a result, we think that the luminescence peak at ~978 nm will not be relevant to the emission band involving the doped i